利用γ-Al2O3替代了60%的Ce/Zr固溶基体，对介孔La/Ce/Zr复合氧化物进行改性。利用ICP分析仪、X射线衍射仪、SEM、比表面仪、激光粒度仪、热重分析仪等表征技术对制备得到的催化剂粉体进行表征。结果显示，活性Al2O3显著提高了催化剂粉体的比表面积，改善了高温下的表面烧结程度，增强了催化剂的热稳定性能并提高了其使用寿命，同时也增加了催化剂粉体的储氧能力和对NO的吸附能力，从而提高了催化活性，明显降低了PM的起燃温度和最高活性工作温度，提高了其对NOx的最大还原率。该研究结果对同时去除船舶柴油机排气污染物PM和NOx具有非常重要的工程应用价值。
A mesoporous La/Ce/Zr composite oxide catalyst was prepared, in whichγ-Al2O3 worked as the main modification component to replace 60wt% of Ce/Zr solid solution matrix. The structures and performances of the composite oxide catalyst powder were characterized by ICP analyzer, X-ray Diffraction(XRD), scanning electron microscope(SEM), specific surface analyzer, laser particle size analyzer, thermal gravimetric analyzer(TGA) and other characterization techniques. The results showed that active Al2O3 modification significantly increased the catalyst powder specific surface areas and improved the sintering degree of the surface under high service temperature, which enhanced the thermal stability of the catalyst and increased its service life. Meanwhile, the oxygen storage capacity and the adsorption capacity to NO are increased also. These characteristics by the Al2O3 modification helped improving the catalytic activity to the reduction of NOx and significantly reducing the ignition temperature and the highest active temperature to PM. The results of this study have an important engineering application value for the simultaneous removal of marine diesel engine exhaust pollutants of PM and NOx.
2017,39(6): 77-82 收稿日期：2016-12-10
DOI：10.3404/j.issn.1672-7619.2017.06.016
分类号：TB331
基金项目：国家自然科学基资助项目（11272213）；上海市科技创新行动计划资助项目（15230501500）
作者简介：郭军武(1970-),男,博士研究生,副教授,轮机长,研究方向为船舶新型材料。
参考文献：
[1] YOSHIDA K, MAKINO S, SUMIYA S, et al. Simultaneous reduction of NOx and particulate emissions from diesel engine exhaust[J]. SAE Paper No. 892046. 1989.
[2] SHANGGUAN W F, TERAOKA Y, KAGAWA S. Promotion effect of potassium on the catalytic property of CuFe2O4 for the simultaneous removal of NOx and diesel soot particulate[J]. Applied Catalysis B-Environmental, 1998, 16(2):149-154.
[3] SHANGGUAN W F, TERAOKA Y, KAGAWA S. Kinetics of soot-O2, soot-NO and soot-O2-NO reactions over spinel-type CuFe2O4 catalyst[J]. Applied Catalysis B-Environmental. 1997, 12(2-3):237-247.
[4] TERAOKA Y, NAKANO K, KAGAWA S. et al. Simultaneous removal of nitrogen-oxides and diesel soot particulates catalyzed by perovskite-type oxides[J]. Applied Catalysis B-Environmental, 1995, 5(3):181-185.
[5] TERAOKA Y, NAKANO K, SHANGGUAN W. et al. Simultaneous catalytic removal of nitrogen oxides and diesel soot particulate over perovskite-related oxides[J]. Catalysis Today. 1996, 27(1-2):107-113.
[6] TERAOKA Y, KANADA K, KAGAWA S. Synthesis of La-K-Mn-O perovskite-type oxides and their catalytic property for simultaneous removal of NOx and diesel soot particulates[J]. Applied Catalysis B-Environmental. 2001, 34(1):73-78.
[7] SHANGGUAN W F, TERAOKA Y, KAGAWA S. Simultaneous catalytic removal of NOx and diesel soot particulates over ternary AB2O4 spinel-type oxides[J]. Applied Catalysis B-Environmental, 1996, 8(2):217-227.
[8] HONG S S, LEE G D. Simultaneous removal of NO and carbon particulates over lanthanoid perovskite-type catalysts[J]. Catalysis Today. 2000, 63:397-404.
[9] SHIBATA K, OI T, OTSUKA A. et al. Properties of DPF system using perovskite catalysts supported on ZrO2/SiC fibers[J]. Journal of the Ceramic Society of Japan. 2003, 111(11):852-856.
[10] LIU X, WEI Y, JIN D, et al. Synthesis of mesoporous aluminum oxide with aluminum alkoxide and tartaric acid[J]. Materials Letters, 2000, 42:143-149.
[11] LIU Zhi, YANG Yuan, MI Jun-hua, et al. Dual-templating fabrication of three-dimensionally ordered macroporous ceria with hierarchical pores and its use as a support for enhanced catalytic performance of preferential CO oxidation[J]. International Journal of Hydrogen Energy, 2013, 38(11):4445-4455.
[12] XIAO Ying, YOU Shu-sen, YAO Yuan, et al. Generalized synthesis of mesoporous rare earth oxide thin films through amphiphilic ionic block copolymer templating[J]. European Journal of Inorganic Chemistry, 2013(8):1251-1257.
[13] WANG Kun (Bridgewater, NJ, US), ROBERT C. Lemon (Easton, PA, US) Robert C. Lemon (Easton, PA, US). MESOPOROUS ALUMINAS STABILIZED WITH RARE EARTH AND PHOSPHOROUS[P]. 20120088654. US:[2012-04-12].
[14] 张海蓉. 柴油机尾气中PM和NOx在复合金属氧化物上同时催化去除的基础研究[D]. 上海:上海交通大学. 2007.ZHANG Hai-rong. Basic research on simultaneous catalytic removal of PM and NOx on the composite metal oxides in diesel exhaust[D]. Shanghai:Shanghai Jiao tong University. 2007.
[15] 于芳丽. 介孔CeO2和Co3O4的制备及其在CO催化氧化中的应用[D]. 大连:大连理工大学. 2013.YU Fang-li. Preparation of mesoporous CeO2 and Co3O4 and their application in catalytic oxidation of CO[D]. Dalian:Dalian University of Technology. 2013.