在某装备的换装施工过程中发现原有筒间密封装置的紧固件和拉伸弹簧出现了腐蚀断裂现象，为了提高装备的海洋环境适应性和使用寿命，某新型筒间密封装置主体结构件和紧固件均采用不锈钢材料，同时主要承压零件由铝合金改为油尼龙材料。为了明确新型筒间密封装置的使用寿命和有限寿命部组件的维修更换周期，本文通过开展模拟实际服役环境下的寿命加速试验，探究并确定筒间密封装置中典型零部件在复杂海洋环境下的使用寿命，作为装备后续维护使用的重要依据。
During the replacement construction of a certain type of launching system, it was found that the fasteners and tension springs of the original inter-tube seal had corrosion fracture. In order to improve the marine environmental adaptability and service life of the equipment, the main structural parts and fasteners of a new inter-tube seal device were made of stainless steel, and the main pressure parts were changed from aluminum alloy to oil nylon. Meanwhile, to clarify the service life of the new inter-tube seal and the maintenance and replacement cycle of components with limited service life, this paper explored and determined the service life of typical parts by carrying out the life acceleration test under the simulated actual service environment, which could be used as an important basis for the subsequent maintenance and use of the equipment.
2022,44(10): 175-179 收稿日期：2021-11-16
DOI：10.3404/j.issn.1672-7649.2022.10.038
分类号：TJ06
作者简介：李四超(1977-)，男，高级工程师，研究方向为水下发射技术
参考文献：
[1] 张晓东, 胡裕龙, 卜世超, 等. 船体钢海水腐蚀研究进展[J]. 装备环境工程, 2018, 15(6): 33–40
[2] 王俊芳, 李希, 殷宗莲, 等. 多因素综合海洋气候模拟加速试验技术在紧固件表面处理工艺筛选中的应用[J]. 表面技术, 2016(2): 175–180
[3] 刘元海. 舰载机载成附件环境适应性设计与管理[J]. 装备环境工程, 2015(1): 73–78
[4] 刘元海. 舰载机载设备腐蚀环境适应性要求的剪裁[J]. 装备环境工程, 2016, 13(5): 61–67
[5] 刘倩倩, 卢琳, 高歌, 等. 大气环境中金属及其保护层霉菌腐蚀研究的进展[J]. 北京科技大学学报, 2017, 39(10): 1463–1469
[6] 梁子原, 林燕顺, 叶德赞, 等. 霉菌对金属材料腐蚀的研究[J]. 海洋学报(中文版), 1986(2): 123–126+136
[7] 刘成臣, 王浩伟, 杨晓华. 不同材料在海洋大气环境下的加速环境谱研究[J]. 装备环境工程, 2013(2): 18–24
[8] 彭京川, 郭赞洪, 杨晓然. 多因素综合海洋气候自然加速试验技术相关性和加速性验证[J]. 装备环境工程, 2016, 13(5): 98–104
[9] 赵建印, 王玺, 刘星. 海军导弹装备结构件腐蚀寿命预测研究[J]. 装备环境工程, 2019, 16(4): 51–54